Aisea ua i ai a matou laei laei e sili ona lelei le teteʻe?

1. O le ufiufi vailaʻau o loʻo taua.

O mea taua a le Wodon ipu o C (%): 3.0-5.0 ma Cr (%): 25-40.

O lenei vaega o vailaʻau e mafua ai le tele o vaega o le Cr7C3 chrome karbida fasimea faigata. Le laʻititi-malo (e oʻo i le HV1800) o nei fasimea i le vaega o le a mautinoa ai se maoaʻe ofuina tetee luga.

wear liner plate with hole01

 

 

 

 

 

 

 

 

 

 

Faatinoga o Galuega:

Mea e faʻataʻitaʻi ai: Quartz one paʻu uili masini suʻega abrasion.

Tulaga: 1. Filifilia tutusa itu faʻataʻitaʻiga mo mea eseese ma ofuina ipu gaosi, ma tuʻu iai i lalo o le tutusa ofuina tulaga galue i a matou meafaigaluega suʻega.

                    2.  45 minute mo faʻataʻitaʻiga taʻitasi

 

                            45 minute mo faʻataʻitaʻiga taʻitasi

text result

 

 

 

 

 

 

 

 

 

 

 

2. Chromium carbide microstructure

O le laei tetee o laei ipu faalagolago tele i luga o le maaa, foliga, lapoʻa, aofaʻi ma tufatufaina o le chromium fasimea maaʻa kareti.

Metallographic structure 01

Metallographic structure 02

 

A oe mafai ona siaki luga o le ata, o le karbida (Cr7C3) voluma vaega i luga o le microstructure o luga 50%.

 

3. Fausia o le malosi i le va o le ufiufi ma le pito i lalo ipu.

O le ufiufi ma le pito i lalo ipu e sili ona fusia faʻatasi. O le ufiufi o le a ulu i totonu o le ipu autu e uiga i 0.8mm-1.8mm, aapa atu e oʻo atu i le 350Mpa ia matou suʻega.

02wear plate bendingx

 

03wear plate with bolts